ACRYLIC AND STYRENE-ACRYLIC POLYMERS
Select product category:
| PRODUCT NAME | POLYMER TYPE | SOLID CONTENT | pH | VISCOSITY | PARTICLE SIZE | MFFT | EMULSIFYING SYSTEM | USES | ||
| Acrynor G251 |
Copolymer | 50±1 | 8±1 | 100-1000 | 0,09-0,15 | 18±1 | Anionic | High setting speed, transparent and gloss film layer, UV radiation durable film | ||
| Acrynor G147 |
Copolymer | 40±1 | 8±0,5 | 70-200 | 0,06-0,09 | 20±2 | Anionic-Nonionic | Transparent layer, water resistance, excellent for wood surface usage | ||
| Acrynor G1481 |
Copolymer | 48±1 | 8±1 | 150-1000 | 0,09-0,15 | 10±1 | Anionic-Nonionic | High loadibility of mineral fillers, water resistance, UV radiation durable film | ||
| Acrynor G1437 |
Copolymer | 43±1 | 8,5±0,5 | 90-300 | 0,05-0,1 | 80±1 | Anionic-Nonionic | High shear resistance, ability of stabilization pigment suspensions, adhesion improvement for metal surfaces, high water resistance and alkali resistance of the film | ||
| Acrynor G1517 |
Copolymer | 50±1 | 8,5±0,5 | 150-400 | 0,15-0,2 | 18±1 | Anionic-Nonionic | High shear resistance, adhesion improvement for metal surfaces, high water resistance and resistance of the film, high stability with anticorrosive pigments. | ||
| Acrynor G1416 |
Copolymer | 40±1 | 8±0,5 | 50-100 | 0,13-0,2 | 3±1 | Anionic-Nonionic | Low film forming temperature, adhesion improvement for mineral surfaces, ammonia free, high water resistance and alkali resistance of the film | ||
| Acrynor G2620 |
Copolymer | 59±1 | 8±0,5 | 900-1700 | 0,15-0,25 | 16±1 | Anionic | High water and alkali resistance, adhesion improvement for mineral surfaces, high setting speed, high shear resistance of the film | ||
| Acrynor G1520 |
Copolymer | 50±1 | 6,5±0,5 | <200 | 0,15-0,25 | 6±1 | Anionic-Nonionic | Excellent compatibility with dry cement mixes, low film forming temperature, high water resistance, high elasticity on temeperatures under 0°, adhesion improvement for metal surfaces | ||
| Acrynor G1522 |
Copolymer | 51±1 | 6,5±0,5 | <200 | 0,2-0,25 | 8±1 | Anionic-Nonionic | Excellent compatibility with dry cement mixes, low film forming temperature, high water resistance, high elasticity on temeperatures under 0°, adhesion improvement for metal surfaces | ||
| Acrynor P1513 |
Copolymer | 50±1 | 8±1 | 7000-12000 | 0,1-0,15 | 20±2 | Anionic-Nonionic | Optimal rheology, resistance to mechanical stirring, good compatibility with coalescents, high pigment filling capacity, high setting speed | ||
| Acrynor D1511 |
Copolymer | 50±1 | 8±0,5 | 100-600 | 0,09-0,13 | N/A | Anionic-Nonionic | Excellent compatibility with dry cement mixes, water resistace | ||
| PRODUCTS | EXTERIOR COATINGS | FACADE PAINTS | FLEXIBLE ROOF COATING | ELASTOMERIC WALL COATINGS | SILICATE PAINTS | CONCRETE PROTECTION | CEMENT MODIFIERS | INTERIOR PAINTS | INTUMESCENT COATINGS |
| Acrynor G251 |  |
|
|
|
|
|
|
||
| Acrynor G147 | |||||||||
| Acrynor G1481 | |
|
|
|
|
||||
| Acrynor G1437 | |
||||||||
| Acrynor G1517 | |
|
|||||||
| Acrynor G1416 | |||||||||
| Acrynor G2620 | |
|
|
|
|||||
| Acrynor G1520 | |
|
|
||||||
| Acrynor G1522 | |
|
|
||||||
| Acrynor P1513 | |
|
|
||||||
| Acrynor D1511 | |
|
|
| PRODUCTS | PRIMERS | MULTIPURPOSE PRIMERS | PENETRATING PRIMERS | BUILDING ADHESIVES | MINERAL BASED SURFACES | PIGMENT PASTES | Wood Coatings | WOOD STAINS | SEALANT |
| Acrynor G251 | |||||||||
| Acrynor G147 | |
|
|||||||
| Acrynor G1481 | |
|
|
|
|
||||
| Acrynor G1437 | |
||||||||
| Acrynor G1517 | |
||||||||
| Acrynor G1416 | |
|
|
|
|
|
|||
| Acrynor G2620 | |
|
|
|
|
|
|||
| Acrynor G1520 | |
|
|
|
|
||||
| Acrynor G1522 | |
|
|
|
|
||||
| Acrynor P1513 | |
|
|
|
|||||
| Acrynor D1511 | |
|
|
|
|
≈ |
| PRODUCT NAME | POLYMER TYPE | SOLID CONTENT | pH | VISCOSITY | PARTICLE SIZE | MFFT | EMULSIFYING SYSTEM | USES | ||
| Acrynor G147 |
Copolymer | 40±1 | 8±0,5 | 70-200 | 0,06-0,09 | 20±2 | Anionic-Nonionic | Transparent layer, water resistance, excellent for wood surface usage | ||
| Acrynor G1481 |
Copolymer | 48±1 | 8±1 | 150-1000 | 0,09-0,15 | 10±1 | Anionic-Nonionic | High loadibility of mineral fillers, water resistance, UV radiation durable film | ||
| Acrynor G1437 |
Copolymer | 43±1 | 8,5±0,5 | 90-300 | 0,05-0,1 | 80±1 | Anionic-Nonionic | High shear resistance, ability of stabilization pigment suspensions, adhesion improvement for metal surfaces, high water resistance and alkali resistance of the film | ||
| Acrynor G1517 |
Copolymer | 50±1 | 8,5±0,5 | 150-400 | 0,15-0,2 | 18±1 | Anionic-Nonionic | High shear resistance, adhesion improvement for metal surfaces, high water resistance and resistance of the film, high stability with anticorrosive pigments. | ||
| Acrynor G1416 |
Copolymer | 40±1 | 8±0,5 | 50-100 | 0,13-0,2 | 3±1 | Anionic-Nonionic | Low film forming temperature, adhesion improvement for mineral surfaces, ammonia free, high water resistance and alkali resistance of the film | ||
| Acrynor G2620 |
Copolymer | 59±1 | 8±0,5 | 900-1700 | 0,15-0,25 | 16±1 | Anionic | High water and alkali resistance, adhesion improvement for mineral surfaces, high setting speed, high shear resistance of the film | ||
| Acrynor G1520 |
Copolymer | 50±1 | 6,5±0,5 | <200 | 0,15-0,25 | 6±1 | Anionic-Nonionic | Excellent compatibility with dry cement mixes, low film forming temperature, high water resistance, high elasticity on temeperatures under 0°, adhesion improvement for metal surfaces | ||
| Acrynor G1522 |
Copolymer | 51±1 | 6,5±0,5 | <200 | 0,2-0,25 | 8±1 | Anionic-Nonionic | Excellent compatibility with dry cement mixes, low film forming temperature, high water resistance, high elasticity on temeperatures under 0°, adhesion improvement for metal surfaces | ||
| Acrynor P1513 |
Copolymer | 50±1 | 8±1 | 7000-12000 | 0,1-0,15 | 20±2 | Anionic-Nonionic | Optimal rheology, resistance to mechanical stirring, good compatibility with coalescents, high pigment filling capacity, high setting speed | ||
| Acrynor D1511 |
Copolymer | 50±1 | 8±0,5 | 100-600 | 0,09-0,13 | N/A | Anionic-Nonionic | Excellent compatibility with dry cement mixes, water resistace | ||
| PRODUCTS | PAPER AND CARDBOARD | ECOLOGICAL PACKAGING | HEAT SEALING COATING | PRIMERS |
| Acrynor P2527 | |
|
||
| Acrynor P25 | |
|
||
| Acrynor P2530 | |
|
||
| Acrynor P1525 | |
|
| PRODUCT NAME | POLYMER TYPE | SOLID CONTENT | pH | VISCOSITY | PARTICLE SIZE | MFFT | EMULSIFYING SYSTEM | USES | ||
| Acrynor T1418 |
Copolymer | 42±1 | 8±1 | 70-150 | 0,15-0,23 | 0 | Anionic-Nonionic | High resistance of the copolymer film to light, heat and aging, high resistance to solutions of weak acids and alkalis, high durability of the copolymer film | ||
| Acrynor T149 |
Copolymer | 40±1 | 8±0,5 | 70-300 | 0,07-0,11 | 23±1 | Anionic-Nonionic | High resistance of the copolymer film to light, heat and aging, high resistance to solutions of weak acids and alkalis, high durability of the copolymer film, water resistance, good compatibility with phenol-, melamine- and urea-formaldehyde resins. | ||
| Acrynor T1526 |
Copolymer | 50±1 | 7±1 | 1000-3000 | 0,22-0,3 | 50±1 | Anionic-Nonionic | High resistance of the copolymer film to light, heat and aging, high resistance to solutions of weak acids and alkalis, high durability of the copolymer film, water resistance, good compatibility with phenol-, melamine- and urea-formaldehyde resins. | ||
| PRODUCTS | NON WOVEN | TEXTILE PRINTING |
| Acrynor T1418 | |
|
| Acrynor T149 | |
|
| Acrynor T1526 | |
|
| PRODUCT NAME | POLYMER TYPE | SOLID CONTENT | pH | VISCOSITY | PARTICLE SIZE | MFFT | EMULSIFYING SYSTEM | USES | ||
| Acrynor G157 |
Copolymer | 50±1 | 8±1 | 5000-8000 | 0,07-0,1 | 17 | Anionic-Nonionic | Good pigment binding capacity, high scrub resistance, perfect for exterior usage | ||
| Acrynor G158 |
Copolymer | 50±1 | 8±1 | 1000-3000 | 0,07-0,1 | 18 | Anionic-Nonionic | Good pigment binding capacity, high scrub resistance, perfect for exterior usage | ||
| Acrynor G159 |
Copolymer | 50±1 | 8±1 | 2000-5000 | 0,07-0,1 | 17,5 | Anionic-Nonionic | Good pigment binding capacity, high scrub resistance, perfect for exterior usage | ||
| Acrynor G1512 |
Copolymer | 50±1 | 8±1 | 800-1500 | 0,1-0,15 | 17 | Anionic-Nonionic | Perfect for facade paint, multi purpose, high scrub resistance | ||
| Acrynor G1509 |
Copolymer | 50±1 | 8±1 | 100-600 | 0,09-0,15 | 20±1 | Anionic-Nonionic | Cold resistance, multi purpose | ||
| Acrynor G1518 |
Copolymer | 50,5±1 | 8±1 | 150-600 | 0,15-0,20 | 26±1 | Anionic-Nonionic | High compatibility with other fillers, good penetration ability , resitant to mechanical stirring, fast setting ability, resistant to low temperatures | ||
| PRODUCTS | EXTERIOR COATINGS | FACADE PAINTS | INTERIOR PAINTS | PRIMERS | MULTIPURPOSE PRIMERS | PENETRATING PRIMERS | MINERAL BASED SURFACES |
| Acrynor G157 | |
|
|
|
|
||
| Acrynor G158 | |
|
|
|
|
||
| Acrynor G159 | |
|
|
|
|
||
| Acrynor G1512 | |
|
|
|
|
||
| Acrynor G1509 | |
|
|
|
|
||
| Acrynor G1518 | |
|
|
|
|
|
|
| PRODUCT NAME | POLYMER TYPE | SOLID CONTENT | pH | VISCOSITY | USES | ||
| Acrynor S30 |
Copolymer | 30±1 | 2,5±0,5 | 60-100 | Preservation of thickening in the area of low shear rates, preventing the deposition of pigments and fillers in containers during storage, ensuring the stability of suspensions with a high content of fillers, while applying , the viscosity decreases at a higher shear rate, which makes it easy to use in paint compositions | ||
| Acrynor S36 |
Homopolymer | 36±1 | 5±1 | 1000-2000 | Soluble in water, improves rheological properties of suspensions, improving the grinding efficiency, compatibility with various binders, ensures the stability of finished formulations | ||
| Acrynor S392 |
Homopolymer | 39±2 | 8±1 | 1000-2000 | A component in the formulations of pigment pastes of water-dispersion paints, putties and plasters for construction purposes | ||
| Acrynor S42 |
Homopolymer | 42±2 | 8±1 | 200-500 | Soluble in water, improves rheological properties of suspensions, improving the grinding efficiency, compatibility with various binders, ensures the stability of finished formulations | ||
| Acrynor S391 |
Homopolymer | 39±1 | 8±0,5 | 50-200 | Soluble in water, improves rheological properties of suspensions, ensures stability of finished sormulations with a high content of fillers, improving the grinding efficiency | ||
| Acrynor S40 |
Homopolymer | 40±1 | 8±1 | >2500 | A component in the formulations of pigment pastes of water-dispersion paints, putties and plasters for construction purposes | ||
| Acrynor S35 |
Copolymer | 30±0,5 | 2,5±0,5 | 60-100 | Preservation of thickening in the area of low shear rates, preventing the deposition of pigments and fillers in containers during storage, ensuring the stability of suspensions with a high content of fillers, while applying , the viscosity decreases at a higher shear rate, which makes it easy to use in paint compositions | ||